Markal® Soldering Flux, Regular, 4 oz, Jar, 6.5 to 7 pH, Paste, Composition: 10 to 20% Ethanolamine Hydrochloride, 10 to 20% Polyethylene Glycol, 10 to 20% Poloxamer, 5 to 15% Ammonium Chloride, 0.1 to 1% 2,6-Di-Tert-Butyl-4-Methylphenol, 0 to 1% Oleic Acid, 0.001 to 1% Sodium Hydroxide, White, Odor/Scent: Faint, >400 deg F Flash, Applicable Materials: Copper, Brass, Galvanized Iron, Lead, Zinc, Tin, Silver, Nickel, Mild Steel, Terne Plate and Malleable Iron
Applicable Materials:
Copper, Brass, Galvanized Iron, Lead, Zinc, Tin, Silver, Nickel, Mild Steel, Terne Plate and Malleable Iron
Color:
White
Type:
Regular
Application Type:
For use with all lead-free and common soft solder, copper, brass, galvanized iron, lead, zinc, tin, silver, nickel, mild steel, terne plate and malleable iron
Capacity:
4 oz
Form:
Paste
Composition:
10 to 20% Ethanolamine Hydrochloride, 10 to 20% Polyethylene Glycol, 10 to 20% Poloxamer, 5 to 15% Ammonium Chloride, 0.1 to 1% 2,6-Di-Tert-Butyl-4-Methylphenol, 0 to 1% Oleic Acid, 0.001 to 1% Sodium Hydroxide
Container Type:
Jar
Flash Point:
>400 deg F
Odor/Scent:
Faint
pH Range:
6.5 to 7
Features
Water soluble paste would not leave residue in water piping|Contains no zinc chloride to reduce corrosion concerns|Non-acid, non-toxic and lead free to eliminate safety concerns|Cleans pipe upon application, allowing solder to run more smoothly around the pipe|All weather formula for use in hot and cold climates|Super detergent action cleans as it solders|Use with all lead free and common soft solders
Standard Approvals
ASTM B813|MIL-F-4995 Type II|NSF 61|UPC Listed